My favorite places to buy materials, especially fabrics, are Composite Envisions and Fiberglast. As of the time I'm writing this I know that we have a 20% discount code from Fiberglast. However, I actually prefer Composite Envisions because you can buy basically everything you need there which means that you can order in bulk. Additionally, their clearance section is better. If you buy from their 2nd quality fabrics, their fibers can get really cheap and rival Fiberglast. 

Fibers

Fiber type

...

Weave	Appearance	Definition	Uses	Pros	Cons
Plain weave		This is one of the most common types of weaves for carbon fiber.  A tow strand in plain weave passes over 1 tow and under 1 tow.	Flat panels (includes sandwich composites)  Bulkheads Tubes	High fabric stability	Poor with curved geometry/complex contours Harsh crimp in the tows due to the short distance between interlaces. The harsh crimp can create stress concentrations which can weaken the part over time.
Plain weave (spread tow)		Like your regular plainweave, but the filaments are spread into a wider tow.	Flat panels (includes sandwich composites) Bulkheads Tubes	Less harsh crimp in comparison to regular plain weave	Poor with curved geometry/complex contours More expensive than regular plain weave
Twill weave (2x2)		This is one of the most common types of weaves for carbon fiber.  If you follow a tow strand in a twill weave it passes over a set number of tows and then under the same number of tows. Since this is 2x2 twill weave, it passes over 2 tows and under 2 tows.  There is a longer distance between tow interlaces which means fewer crimps.	Curved geometry Typically bottom shell, canopy	Flexible  Can conform to complex contours Fewer crimps compared to plain weave thus less potential stress concentrations.	Less fabric stability than plain weave
Twill weave (3x3, 4x4, etc)		Twill weave with less formability than standard 2x2 twill weave. The weave is less tight than 2x2 twill. We have historically rarely/never used this, but if you need to make a composite with many complex, tight curves then you may want to consider this. There is an even longer distance between tow interlaces which means fewer crimps than regular twill weave	Curved geometry Typically bottom shell, canopy		More expensive than regular twill weave Less fabric stability than 2x2 twill weave

...

1. After you have determined all of your fabric qualities, you need to calculate how much fiber you are going to use. The best way to do this is to go into the CAD file of the aeroshell and then create rectangular sketches that are the size of the fiber rolls that you plan to buy. 
   1. Make sure you have 3-5 inches of overlap for each layer of fiber.
2. Find the area of these rectangular sketches
3. Know how much ply you want in your composite, and then multiply the area by the number of ply.
4. Then, add 50% to the final amount you get.
   1. You will always need more than you think. People will never cut fiber optimally or lay down fiber optimally. When I ordered material, I had a 30% buffer and it was not enough.

Resin 

• Pot life determines how long you have to work with the resin in a pot/bucket before it starts to cure. Most laminating resins that cure at room temperatures have a really low pot life.
  • Higher pot life gives more leniency.

Mold Smoothers

• Joint compound: https://www.homedepot.com/p/USG-3-5-gal-Soquete-Ready-Mixed-Joint-Compound-380066/202329615
  • We use this and it sucks and makes mold release horrible. Please find an alternative mold sealant that is not joint compound
• Spackle
• Bondo: This is used on composite to patch gaps

Vacuum Materials

• Vacuum bag
  • Stretchy vacuum bag such as Stretchlon 200 is basically a necessity for any layup that isn't relatively thin. 
    • https://www.fibreglast.com/product/stretchlon-200-bagging-film-1678

• Breather: 
  • Breather is separated by density. Which one you choose is not that important as long as its roll width is wide enough for the composite you want to make. I chose based on price.
• Tacky tape
  • We use any kind of yellow tacky tape. Yellow tacky tape performs well in hotter temperatures and it is higher quality.
  • Avoid gray tacky tape. It can be used for test composites or smaller composites but I would strongly advise against using these for anything that's important.

PPE

Leads, encourage your facilities lead beforehand to buy protective gear. This way three teams don't have to buy stuff, rather OB buys stuff.

Step-by-step guide